Refractory Silicon Brick Used in Glass Kiln

Ref Price:

Loading Port:: Tianjin

Payment Terms:: TT OR LC

Min Order Qty:: 20 m.t.

Supply Capability:: 5000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

CALCINED BAUXITE A

Gas Calcined Anthracite Coal made from taixi Anthracite

Calcined Bauxite Rotary Kiln Al2O3 85%

Calcined Bauxite Rotary Kiln Al2O3 86%

Metallurgical Grade Aluminum Oxide Al2O3 Powder

$Best Calcined Bauxite for Refractory Raw Materials$

Best Calcined Bauxite for Refractory Raw Materials

86% alumina 1-3mm calcined bauxite with low price

$80% Round Kiln Alumina Calcined Bauxite Refractory Raw Material$

80% Round Kiln Alumina Calcined Bauxite Refractory Raw Material

General Information:

CMAX brand Silica bricks are made from high quality quartz tail sand, lime and mineralizing agent through the process of crashing, screening, mixing, pressing, drying and sintering.

Features of Refractory silica bricks for Glass Kiln:

1. high volume density of 2.34 g/cm3

2. high SiO2 content of 96%

3. low iron content of 0.8%

4. low melting point of 5%

Applications of Refractory silica bricks for Glass Kiln:

Because of the high temperature resistant performance significantly, long service life characteristics (as long as more than eight years) of refractory silica brick for Glass Kiln, it can significantly improve the quality of glass, so the refractory silica bricks are widely used in all kinds of glass furnace melting department, regenerator and other important parts.

Physical and chemical index of refractory silica bricks for glass kiln:

Item Brand		CMAX-96A	CMAX-96B
Item Brand		CMAX-96A	CMAX-96B
SiO2 % ≥		96	96
Al2O3+2(K2O+Na2O) % ≤		0.5
Fe2O3 % ≤		0.8	1
Refractoriness °C ≥		1710	1710.0
0.2MPa Refractoriness under load °C ≥		1680	1670
Apparent porosity % ≤	Brick with weight no less than 20kg	20	20
Apparent porosity % ≤	rick with weight less than 20kg	22	22
CS MPa ≥		35	35
Bulk desity g/cm3 ≤		2.34	2.34

Starndard Size:

230*114*64mm

230*114*76mm

$Refractory Silicon Brick Used in Glass Kiln$

Q:What is unshaped refractory?: Plastic. From the production method, the plastic is between the concrete and the castable. It is made of refractory material by refractory material plant, which is made of plastic clay. The ingredient is a retarder. It is packaged by plastic bag, and construction and heat treatment are carried out on the spot. But the biggest problem is the application of plastic on the knotted Jiecha easy peeling, retarder dosage improper or is vulnerable to bad caking plastic hardening.

Q:What are the electrical fire protection materials?: Electrical fire protection materials are the following: 1, fire proof board It is the most commonly used materials in the market, which has the advantages of fire prevention, moisture, abrasion, oil, easiness to clean, and more varieties of colors. Installed in the building exit corridors, stairs and corridors, such as fire ceiling ceiling, it can ensure that people can be evacuated safely, and to protect people from the spread of the fire. 2, fire proof door, fire proof door is divided into wooden fire door, steel fire door and stainless steel fire door. Fire proof doors are usually used for the opening of the firewall, the entrance of the staircase, the evacuation of the aisle, the openings and other parts of the pipeline, the fire prevention, playing an important role in reducing the loss of fire. 3, fire shutter It can be set in the location where it is not convient to install a fire proof wall, fire shutter generally has functions such as good fire resistance, heat insulation, smoke, compression, anti aging, wear and corrosion. 4, fireproof and mothproof wood fire wood moth is made by putting ordinary wood into the solution containing calcium and aluminum, and then into the solution containing phosphate and silicate. In this way, two ion will be undergong chemical reaction in the wood, forming materials similar to the ceramic, and filling the gap of cells and tissues, so that allowing it to have fireproof and mothproof performance.

Q:How long can gypsum board endure fire?: General gypsum plaster board with a thickness of less than 12mm has a fire endurance which is less than half an hour. Scheme One of gypsum board partition system by using 75# series of lightgage steel joist: separation distance of keels keep 600mm in vertical direction. The thickness is greater than 0.5mm; gypsum board: it shoule be the board of double-sided and single-layer with the thickness of 12mm. Fire-resistant gypsum plaster board's fire-resistance limit: 1 hour. Sound insulation index: over 35 rwdb.

Q:Does the refractory material used in steelmaking all refer to refractory brick?: It includes not only refractory brick but also unshaped refractory; while the foaming?agent, ladle filler sand and deoxidizer are not refractory materials but ferrous metallurgy auxiliary materials.

Q:What are the requirements when producing fireproof materials by kaolin?: Kaolin refractories in fact play a role in two aspects, one is to improve the refractoriness, the second is to improve plasticity of the the refractory . Aluminum content the higher the better, of course, but kaolin is not the only material to improve the content of aluminum, using materials that contain higher content of aluminum such as the bauxite chamotte. So the content of kaolin aluminum does not have to be too high. over 38% is fine. viscosity is important and strong viscidityis better without having to add bentonite. Refractoriness above 1400 degrees is enough.

Q:What's the heat conductivity coefficient of fire-resistant material?: There are many types of fire-resistant materials woth different thermal conductivity. The question should be more specific.

Q:how to use boiler fireclay: Boiler refractory, diluted with water to touch the places where needed, can be used after high temperature baking.

Q:what kind of fireproof materials is used for high rise buildings?: Recommended thickness of 1mm or more # 304 stainless steel, refractory, corrosion-resistant, easy to clean. closed balcony of high rise buildings use thickened manganese, aluminum profiles. You can also use plastic steel window, solid wooden windows. Mg-Mn alloys have excellent weldability and corrosion resistance, unstressed corrosion tendency. Mechanical properties are not good enough, the ultimate strength of 210 ~ 280MPa.

Q:how to classify the fireproofing material levels A1 A2 B1?: their classification is shown specifically in Fireproof? Specification of Building Interior Decoration?Design GB 50222-95 appendix A, flammability,inflammability materials, flame retardency, noninflammability: combustion performance of A, B3, B2, B1 materials are divided into

Q:Which refractory is better for building 1500 degree kiln ?: High alumina brick or 99 alumina hollow ball brick is OK, which can withstand a temperature of 1600 ℃.

1. Manufacturer Overview
Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates
a) Certification Name
Range
Reference
Validity Period

3. Manufacturer Capability
a)Trade Capacity
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range